牌號 | Carpenter Stainless Type 305 |
廠家 | Carpenter Technology Corporation |
分類 | Steel |
介紹 | Carpenter Stainless Type 305 has been used for severe cold forming operations. The higher nickel content lowers the tendency to work-harden, so that a greater amount of deformation is possible before process annealing is necessary. Having the highest nickel content of the austenitic stainless steels considered to be in the 18-chromium 8-nickel family, Carpenter Stainless Type 305 has the lowest rate of strain hardening of these steels. Carpenter Stainless Type 305 has also been used where the finished part must remain nonmagnetic after severe cold working. Carpenter Stainless Type 305 has been used extensively for parts produced by deep drawing. This steel has worked well in automatic eyelet machines when the part was produced without process annealing. Type 305 should be considered for cold headed bolts, screws, etc. Because of its nonmagnetic properties, Carpenter Stainless Type 305 should also be considered for use in electrical instrumentation. |
Carpenter Technology Corporation 產(chǎn)品展示 | 種類 |
---|---|
Carpenter SCF 260? Alloy | Steel |
Consumet? Electrical Iron | Steel |
KnightCote? Wire Coating | Steel |
Carpenter 15Cr-5Ni | Steel |
Micro-Melt? Maxamet? Alloy | Steel |
Carpenter 21Cr-6Ni-9Mn | Steel |
Carpenter 275 Stainless | Steel |
AerMet? 340 Alloy | Steel |
Carpenter? CTS? BD1 Alloy | Steel |
Carpenter No. 345 | Steel |
訂購說明