| 斷裂伸長率 | 2% | 拉伸強度 | 45MPa | 密度 | 1.02g/cm3 |
| 熔體流動速率 | 7.5g/10min | 缺口沖擊強度 | 16 |
|
|
產(chǎn)品簡述
| 斷裂伸長率 | 2% | 拉伸強度 | 45MPa | 密度 | 1.02g/cm3 |
| 熔體流動速率 | 7.5g/10min | 缺口沖擊強度 | 16 |
詳細數(shù)據(jù)
訂購指南
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 體積密度 | ASTM D-1895 | 0.60 | g/cm3 | |
| 熔體流動速率 | 200℃,5kg | ASTM D-1238 | 7.5 | g/10min | |
| 密度 | ASTM D-792 | 1.02 | g/cm3 | ||
| 機械性能 | 最終拉伸強度 | ASTM D-638 | 45 | MPa | |
| IZOD沖擊強度 | ASTM D-256 | 16 | J/M | ||
| 洛氏硬度 | ASTM D-785 | 93 | L scale | ||
| 拉伸模量 | ASTM D-638 | 2990 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 60 | M scale | ||
| 彎曲強度 | ASTM D-790 | 66 | MPa | ||
| 最終拉伸伸長率 | ASTM D-638 | 2 | % | ||
| 彎曲模量 | ASTM D-790 | 3627 | MPa | ||
| 熱性能 | 熱變形溫度 | ASTM D-648 | 100 | ℃ | |
| 阻燃性 | HB | CLASS | |||
| 維卡軟化點 | ASTM D-1525 | 102 | ℃ | ||